Jump to content

Recommended Posts

Posted

I was impressed with the project, workmanship and video production and thought you guys might enjoy it.    A neat piece work with a rather complex 'secret' stepped lock - hang in there to the end to see how it operates. 

 

 

  • Like 2
Posted (edited)

Fantastic piece of work and craftsmanship. But I'm a bit puzzled what's the idea of it? For safekeeping? Sure the box on its own would be heavy, but still transportable. Next, chances are that the value of the box is higher than its contents. Is it a show-piece to show off his excellent skills? Or is it to admire ......... because it is for sure admirable ........ !

Another possibility is a combination of all the above :)

Edited by Endeavor
Posted (edited)
32 minutes ago, Endeavor said:

Another possibility is a combination of all the above :)

I have no idea, possibly a commission?   art?  reminiscent of historical creations back when a lock box really mattered?  I don't think I'd set out to build one but in a way its lot like a finely made, expensive mechanical watch;  you don't really need one to tell time just like you don't need that box to keep things secure , but you like them just because they are such a mechanical marvels of craftsmen,  an achievement of the human spirit and all.  Best I can come up with anyway :)

Edited by measuretwice

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.
Note: Your post will require moderator approval before it will be visible.

Guest
Reply to this topic...

×   Pasted as rich text.   Restore formatting

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

  • Recently Browsing

    • No registered users viewing this page.
  • Topics

  • Posts

    • This is a modern watch, the crown is definitely made from solid 316l steel. You must have heated the crown to some 200C caused the surface colour to change to light yellow. It's similiar to steel tempering. Yes it is the chromium oxide that forms during the heating that gives rise to the colours you see as you know stainless steel contains chromium. The fact the crown is SS lead me to a question, you've never heard of the alum method? Because alum would work perfectly in this case, instead of drilling, which, there is always a risk of damaging the crown, I would just let the crown chilling in some warm alum solution for 1-2 days and the job is done.   Sure can but the thing is the crown is not just mirror finishing, the lock symbol is polish while its background is some sand-blasted finishing so it would be hard to replicate that. You can buff it all shiny but losing the sand-blasted finishing means it won't look exactly like before.   Gasket is always tricky to me. I would try to use some gasket that look closest to the broken one in term of thickness and diameter, and check if the replacement gasket fit with some friction to the case tube. Lastly you can still use alum at this point.
    • No mate. Sorry if that offends you! Also please don’t take threads off-topic. I thank you sir. 
    • Hello and welcome from Leeds, England. 
    • Thanks Mark I have uBlock Origin Lite add-on for my Windows Chrome browser, so I've never seen a single ad on this site ! It also removes all adds from Youtube - I couldn't bear to watch it without uBlock
    • Thanks Mark, but can we still discuss the other important matter please and not be distracted from it. Thank you.
×
×
  • Create New...